What can be the root cause of SMT LED Component Shift during reflow?
Ask the Experts

View the Expert comments below.
,{url:'http://www.circuitinsight.com/videos/experts_final.mp4'}], clip:{autoBuffering:true, autoPlay:true, scaling:'scale' } }).ipad();

Arranged via association with Circuitnet..
See the Expert Panel | Submit A Questions | Join the Panel
Ask the Experts Question
Ask the Experts
LED Component Shift During Reflow
LED Component Shift During Reflow
What can be the root cause of SMT LED Component Shift during reflow? See the photo.
M.M.
Expert's Panel Responses
Shift can result from insufficient channels for out gassing of the solder paste vehicles during reflow. One way to correct this is to window pane the stencil aperture which leaves channels for outgassing during reflow.
image
Bill Coleman
Vice President Technology
Photo Stencil
For over 18 years, Dr. Coleman has been the vice president of technology for Photo Stencil, working closely with customers to understand their printing requirements. His efforts have resulted in several new stencil products.
One of the most common reasons for a component to shift during reflow is that it is "floating." The reason a component could float is by applying too much solder paste during the stencil printing process. My recommendation is to verify both the pad and aperture design. I would use the manufacturers recommended design as a start, and IPC recommended in case the manufacturer doesn't have any processing details in their datasheet. Also a consideration is the thickness of the stencil.  

Once you establish a baseline using a good starting point, if you still have the shifting you can adjust the aperture design by doing a reduction. Either a straight percent reduction or pulling paste away from the part to reduce float. When doing this, it is always best to record and document your experiments for future reference.
image
Walter Pierowski
Process Engineer
Esterline Interface Technologies
Mr. Pierowski is currently a Process Engineer for SMT and Electrical Assembly with 20+ years of experience. A majority of the experience was based in screen/stencil printing for electronics manufacturing including application support for SMT, LTCC, HTCC and thick film.
Check your profile.  There is a possibility that outgassing is causing the shifting of LED's.
image
Edithel Marietti
Senior Manufacturing Engineer
Northrop Grumman
Edithel is a chemical engineer with 20 year experience in manufacturing & process development for electronic contract manufacturers in US as well as some major OEM's. Involved in SMT, Reflow, Wave and other assembly operations entailing conformal coating and robotics.
Probably floating on too much flux or alloy. Try cross hatching pad.
Greg York
Technical Sales Manager
BLT Circuit Services Ltd
Greg York has over thirty two years of service in Electronics industry. York has installed over 600 Lead Free Lines in Europe with Solder and flux systems as well as Technical Support on SMT lines and trouble shooting.
Depending on the amount of solder on the pad, the LED can become buoyant and "float around" on the surface of the molten solder. This can further be aggravated when reflowed in a convection reflow oven where the fans can actually blow parts around.  

I hope that it goes without saying, but I was also check the placement before reflow, make sure the boards are not getting bumped and that operators did not place or reposition these parts manually.
image
Kay Parker
Technical Support Engineer
Indium Corporation
Kay Parker is a Technical Support Engineer based at Indium Corporation's headquarters in Clinton, N.Y. In this role she provides guidance and recommendations to customers related to process steps, equipment, techniques, and materials. She is also responsible for servicing the company's existing accounts and retaining new business.
There many root causes for components drift during SMT reflow process:
  1. Ramp up rate too high at reflow stage. High ramp up rate will cause excessive flux outgassing and pushes the component away from the original position.
  2. Vibration or sudden speed change during the reflow process.
  3. Component or board oxidation. Heavily oxidized components and boards will cause uneven wetting during the reflow.
  4. Insufficient flux activity on solder paste, which will also cause uneven wetting on two sides of the component.
  5. Excess solder paste deposition (stencil too thick). High volume of molten solder will cause component floating at reflow stage.
  6. Solder paste misregistration during the stencil printing or inaccurate component placement.
  7. Uneven heating on two sides of the component. This can be caused by either asymmetrical heat sink effect or ramp up rate too high at reflow zone.
image
David Bao
Director New Product Development
Metallic Resources, Inc
David Bao has more than fifteen years of experience in developing new solder paste, wave soldering fluxes and other SMT consumables. He currently serves as the Director of New Product Development at Metallic Resources Inc. He received a Ph.D. in Chemistry at Oklahoma State University.
Submit A Comment

Comments are reviewed prior to posting. Please avoid discussion of pricing or recommendations for specific products. You must include your full name to have your comments posted. We will not post your email address.

Your Name


Company


E-mail


Country


Comments


Authentication

Please type the number displayed into the box. If you receive an error, you may need to refresh the page and resubmit the information.



Related Programs
bullet Analysis of Laminate Material Properties for Correlation to Pad Cratering
bullet Novel Approaches for Minimizing Pad Cratering
bullet Acceptable Rate for Head in Pillow?
bullet LED Component Shift During Reflow
bullet Testing PCBs for Creep Corrosion
bullet Contaminated Joints Cause an Assembly to Fail RoHS Compliance
bullet Mitigating Tin Whiskers in Alternative Lead-Free Alloys
bullet Components Falling Off During Wave Soldering
bullet Dust contamination after selective soldering
bullet Human-Induced Contamination on PCB Assembly
More Related Programs